261 Blue Flux Coated General Purpose Silver Brazing Alloy 1/16X18
Kent Item # EG26170000
Brand: Kent Automotive
A low working temperature silver brazing alloy with superb wetting action on difficult-to-join metals such as tool steels, stainless steel, beryllium copper and nickel alloys.
Read More
Territory Pricing:
Pricing and promotional offers are available to customers located in
Grey-Bruce and other approved territory areas. Once your territory is
validated, any available list price and eligible promotion will display here.
Package: Pack of 6
Shipping charges as per Kent Automotive will be applicable and billed as per
your standard agreement and account setup.
Product Description
A low working temperature silver brazing alloy with superb wetting action on difficult-to-join metals such as tool steels, stainless steel, beryllium copper and nickel alloys.
• Fast Flowing – Works well on tight joints
• High Silver Content – Lower melting point and reduces need for high heat for joining
• High-detergent conductivity
• High strength
• Corrosion resistant
• Cadmium-free
• Joint Strength: Up to 60,000 PSI/414 Mpa
• Elongation: 32%
• Working Temperature: 1370°F/743°C
• Electrical Conductivity: 19% IACS
• Corrosion Resistance: Good
• Coating: Blue
PROCEDURES Clean the weld area. Remove all rust, paint, grease, oil and other foreign matter. Maintain joint clearance of 0.003” to 0.005”. Prefluxing is not required; however, additional flux will help in tight joints and may be needed. Heat the weld area to a dull red color using a slightly carburizing flame. Melt off a small amount of alloy and flux. Keep the torch in motion and flow the deposit through the joint. Allow to cool slowly. Remove flux residue with warm water.
• Fast Flowing – Works well on tight joints
• High Silver Content – Lower melting point and reduces need for high heat for joining
• High-detergent conductivity
• High strength
• Corrosion resistant
• Cadmium-free
• Joint Strength: Up to 60,000 PSI/414 Mpa
• Elongation: 32%
• Working Temperature: 1370°F/743°C
• Electrical Conductivity: 19% IACS
• Corrosion Resistance: Good
• Coating: Blue
PROCEDURES Clean the weld area. Remove all rust, paint, grease, oil and other foreign matter. Maintain joint clearance of 0.003” to 0.005”. Prefluxing is not required; however, additional flux will help in tight joints and may be needed. Heat the weld area to a dull red color using a slightly carburizing flame. Melt off a small amount of alloy and flux. Keep the torch in motion and flow the deposit through the joint. Allow to cool slowly. Remove flux residue with warm water.
Technical Specifications
| Item#: | EG26170000 |
|---|---|
| Welding Process | Brazing |
| Type | Flux-Coated Brazing Rod |
| Diameter | 1/16 " |
| Length | 18 " |
| Tensile Strength | 70,000 PSI |
| Melting Temperature | 1,295 °F |
| Color | Blue |
| Base Metal | All Metals Except White Metals |
| Recommended Flux | 361 |
| UNSPSC #: | 23271804 |
| TAA Compliant: | Yes |
| Weight | 0.395 |
| lb | Product Resources |