52 Aluminum/Zinc Bare Brazing Rod 1/8"
Kent Item # CW1735
Brand: Cronatron®
A selection of alloys for joining all types of aluminum. Superior Advantages
Read More
Territory Pricing:
Pricing and promotional offers are available to customers located in
Grey-Bruce and other approved territory areas. Once your territory is
validated, any available list price and eligible promotion will display here.
Package: Pack of 2
Shipping charges as per Kent Automotive will be applicable and billed as per
your standard agreement and account setup.
Product Description
A selection of alloys for joining all types of aluminum.
Superior Advantages
• Products for joining and buildup
• Easy to apply
High-strength, self-fluxing
Tensile Strength: 40,000 PSI
Bond Strength: 28,000 PSI
Application Temperature: 720°F (382°C)
Typical Applications
• Aluminum frames
• Tubing and piping
• Ornamental aluminum
• Cast aluminum
Usage ProcedureHeat base metal with 1-X acetylene feather flame. Melt off small amount of Cronabraze Eagle™ 52 and scrub (tin) area of repair using a clean stainless steel wire brush. Use circular motion of torch when applying buildup or repair alloy. Copper or carbon block is suggested as a chill bar when soldering thin sections. No flux is required.
Technical TipMaximum bonding requires getting to the base metal under the oxide layer present on all aluminum. To bond to virgin metal, scrub the bonding area with molten ‘52’ alloy or scratch the area with the ‘52’ alloy with the base metal at application temperature. Heavy oxide layers can be easily removed with ‘Flex’ grinding wheels.After tinning, bring filler to surface at 90° angle and manipulate torch in a circular motion at 45°. Avoid overheating base metal. Use clean torch tip to p
Superior Advantages
• Products for joining and buildup
• Easy to apply
High-strength, self-fluxing
Tensile Strength: 40,000 PSI
Bond Strength: 28,000 PSI
Application Temperature: 720°F (382°C)
Typical Applications
• Aluminum frames
• Tubing and piping
• Ornamental aluminum
• Cast aluminum
Usage ProcedureHeat base metal with 1-X acetylene feather flame. Melt off small amount of Cronabraze Eagle™ 52 and scrub (tin) area of repair using a clean stainless steel wire brush. Use circular motion of torch when applying buildup or repair alloy. Copper or carbon block is suggested as a chill bar when soldering thin sections. No flux is required.
Technical TipMaximum bonding requires getting to the base metal under the oxide layer present on all aluminum. To bond to virgin metal, scrub the bonding area with molten ‘52’ alloy or scratch the area with the ‘52’ alloy with the base metal at application temperature. Heavy oxide layers can be easily removed with ‘Flex’ grinding wheels.After tinning, bring filler to surface at 90° angle and manipulate torch in a circular motion at 45°. Avoid overheating base metal. Use clean torch tip to p
Technical Specifications
| Item#: | CW1735 |
|---|---|
| Welding Process | Brazing |
| Type | Bare Brazing Rod |
| Diameter | 1/8 " |
| Length | 18 " |
| Tensile Strength | 28,000 PSI |
| Melting Temperature | 720 °F |
| Base Metal | Aluminum/Zinc |
| UNSPSC #: | 23271804 |
| TAA Compliant: | Yes |
| Weight | 2.5 |
| lb | Product Resources |